Long Service Life Periclase Brick Used In Cement Kiln with Apparent Porosity of 13-16%

Product Categories
Henan Hongtai Kiln Refractory Co.,Ltd.
Trust Seal
Verified Supplier
Credit Check
Supplier Assessment
Contact Now

Long Service Life Periclase Brick Used In Cement Kiln with Apparent Porosity of 13-16%

Place of Origin : Henan, China

Shape : Block

Material : Alumina Block

SiO2 Content (%) : 0.6%

Al2O3 Content (%) : 9-12%

MgO Content (%) : 87-90%

CaO Content (%) : 1.5%

Refractoriness (Degree) : 1770°< Refractoriness< 2000°

CrO Content (%) : -

SiC Content (%) : -

Model Number : HT

Brand Name : HongTai

Processing Service : Bending, Welding, Punching, Decoiling, Cutting, Moulding

Bulk density(g/cm3) : 2900-3050kg/m3

Size : Customized Size

Color : Yellow

Cold crushing strength/Mpa : 55~90

Apparent porosity/% : 13-16%

Working temperature : 1600-1900

Name : Magnesia Iron Spinel Bricks

Packaging Details : in wooden pallets

Supply Ability : 200000 Carton/Cartons per Month Magnesia Iron Spinel Bricks

MOQ : 10 cartons

Price : $1,000.00 - $1,200.00/cartons

Contact Now

Details Images
Details Images
Long Service Life Periclase Brick Used In Cement Kiln with Apparent Porosity of 13-16%
Long Service Life Periclase Brick Used In Cement Kiln with Apparent Porosity of 13-16%
Long Service Life Periclase Brick Used In Cement Kiln with Apparent Porosity of 13-16%
Long Service Life Periclase Brick Used In Cement Kiln with Apparent Porosity of 13-16%
Magnesia Alumina Spinel Brick
It takes good quality fused magnesite and fused mgo-cr clinker as raw material, formed under high pressure,burned in high
temperature. It has character of corrosion resistance.
Main using for VOD,AOD,SKF,LF,RH etc. secondary refining furnace.

Advantage

Products with anti- alkaline corrosion ability, anti-erosion ability, good thermal stability, high strength , less pollution,RUL
advantages
Detail Specification
Detail Specification
FM-MA80
FM-MA85
FM-MA90
MgO %
85
88
90
Al2O3 %
7
6.5
6.5
SiO2 %
4
2.4
1.2
CaO %
1.5
1.3
1.2
Fe2O3 %
1.7
1.4
1.0
Apparent porosity %
17
17
17
Bulk density (g/cm3)
2.93
2.93
2.94
Cold crushing strength (MPa)
50
50
55
Refractoriness under load (°C)
1610
1650
1700
Thermal shock resistance (times)
3-6
3-6
3-6
Standard size: 230 x 114 x 65 mm ,Special size and OEM Service also provide
The size is precise, providing kinds of shapes according to customer's drawing
Long Service Life Periclase Brick Used In Cement Kiln with Apparent Porosity of 13-16%
Long Service Life Periclase Brick Used In Cement Kiln with Apparent Porosity of 13-16%
Long Service Life Periclase Brick Used In Cement Kiln with Apparent Porosity of 13-16%
Long Service Life Periclase Brick Used In Cement Kiln with Apparent Porosity of 13-16%
Long Service Life Periclase Brick Used In Cement Kiln with Apparent Porosity of 13-16%
Long Service Life Periclase Brick Used In Cement Kiln with Apparent Porosity of 13-16%
Long Service Life Periclase Brick Used In Cement Kiln with Apparent Porosity of 13-16%







Long Service Life Periclase Brick Used In Cement Kiln with Apparent Porosity of 13-16% Manufactures

Long Service Life Periclase Brick Used In Cement Kiln with Apparent Porosity of 13-16% Images