High Temperature Resistance Magnesium Aluminum Spinel Brick for Cement Rotary Kiln Made

Place of Origin : Henan, China

Shape : Block

Material : Alumina Block

SiO2 Content (%) : 0.6%

Al2O3 Content (%) : 9-12%

MgO Content (%) : 87-90%

CaO Content (%) : 1.5%

Refractoriness (Degree) : 1770°< Refractoriness< 2000°

CrO Content (%) : -

SiC Content (%) : -

Model Number : HT

Brand Name : HongTai

Processing Service : Bending, Welding, Punching, Decoiling, Cutting, Moulding

Bulk density(g/cm3) : 2900-3050kg/m3

Size : Customized Size

Color : Yellow

Cold crushing strength/Mpa : 55~90

Apparent porosity/% : 13-16%

Working temperature : 1600-1900

Name : Refractory Magnesium Aluminum Spinel Brick

MOQ : 10 cartons

Price : $1,000.00 - $1,200.00/cartons

Contact Now

Details Images
Details Images
High Temperature Resistance Magnesium Aluminum Spinel Brick for Cement Rotary Kiln Made
High Temperature Resistance Magnesium Aluminum Spinel Brick for Cement Rotary Kiln Made
High Temperature Resistance Magnesium Aluminum Spinel Brick for Cement Rotary Kiln Made
High Temperature Resistance Magnesium Aluminum Spinel Brick for Cement Rotary Kiln Made
Magnesia Alumina Spinel Brick
It takes good quality fused magnesite and fused mgo-cr clinker as raw material, formed under high pressure,burned in high
temperature. It has character of corrosion resistance.
Main using for VOD,AOD,SKF,LF,RH etc. secondary refining furnace.

Advantage

Products with anti- alkaline corrosion ability, anti-erosion ability, good thermal stability, high strength , less pollution,RUL
advantages
Detail Specification
Detail Specification
FM-MA80
FM-MA85
FM-MA90
MgO %
85
88
90
Al2O3 %
7
6.5
6.5
SiO2 %
4
2.4
1.2
CaO %
1.5
1.3
1.2
Fe2O3 %
1.7
1.4
1.0
Apparent porosity %
17
17
17
Bulk density (g/cm3)
2.93
2.93
2.94
Cold crushing strength (MPa)
50
50
55
Refractoriness under load (°C)
1610
1650
1700
Thermal shock resistance (times)
3-6
3-6
3-6
Standard size: 230 x 114 x 65 mm ,Special size and OEM Service also provide
The size is precise, providing kinds of shapes according to customer's drawing
High Temperature Resistance Magnesium Aluminum Spinel Brick for Cement Rotary Kiln Made
High Temperature Resistance Magnesium Aluminum Spinel Brick for Cement Rotary Kiln Made
High Temperature Resistance Magnesium Aluminum Spinel Brick for Cement Rotary Kiln Made
High Temperature Resistance Magnesium Aluminum Spinel Brick for Cement Rotary Kiln Made
High Temperature Resistance Magnesium Aluminum Spinel Brick for Cement Rotary Kiln Made
High Temperature Resistance Magnesium Aluminum Spinel Brick for Cement Rotary Kiln Made
High Temperature Resistance Magnesium Aluminum Spinel Brick for Cement Rotary Kiln Made







High Temperature Resistance Magnesium Aluminum Spinel Brick for Cement Rotary Kiln Made Manufactures

High Temperature Resistance Magnesium Aluminum Spinel Brick for Cement Rotary Kiln Made Images

Inquiry Cart 0
Send your message to this supplier
 
*From:
*To: Henan Hongtai Kiln Refractory Co.,Ltd.
*Subject:
*Message:
Characters Remaining: (0/3000)
 
You May Like